Изображения могут отличаться от продукта. Подробнее см. технические характеристики.
Standard
GB,ASTM/AISI,ГОСТ,BS,JIS,NF,DIN / VDEh,DIN / VDEh
Материал
Alumina, Silicon Nitride, Silicon Carbide, Zirconia, Boron Nitride
Номинальный диаметр (Dw)
0.3mm-114.3mm
Твердость
70-90HRC
Плотность
3.1-6g/cm3
| NO. | Product | Product Number | Плотность | Твердость | Вес | Материал | Номинальный диаметр (Dw) |
|---|---|---|---|---|---|---|---|
| 101 |
|
Ceramic Ball 1 11/16inch | 3.20-3.30 g/cm3 | 75-80 HRC | 131.94140 g | Silicon Nitride | 1.68750 inch |
| 102 |
|
Ceramic Ball 1 3/4inch | 3.20-3.30 g/cm3 | 75-80 HRC | 147.15123 g | Silicon Nitride | 1.75000 inch |
| 103 |
|
Ceramic Ball 45mm G10 | 3.20-3.30 g/cm3 | 75-80 HRC | 152.68140 g | Silicon Nitride | 45.00000 mm |
| 104 |
|
Ceramic Ball 1 13/16inch | 3.20-3.30 g/cm3 | 75-80 HRC | 163.48721 g | Silicon Nitride | 1.81250 inch |
| 105 |
|
Ceramic Ball 1 7/8inch | 3.20-3.30 g/cm3 | 75-80 HRC | 180.98957 g | Silicon Nitride | 1.87500 inch |
| 106 |
|
Ceramic Ball 1 15/16inch | 3.20-3.30 g/cm3 | 75-80 HRC | 199.69853 g | Silicon Nitride | 1.93750 inch |
| 107 |
|
Ceramic Ball 50mm G10 | 3.20-3.30 g/cm3 | 75-80 HRC | 209.43951 g | Silicon Nitride | 50.00000 mm |
| 108 |
|
Ceramic Ball 2inch | 3.20-3.30 g/cm3 | 75-80 HRC | 219.65431 g | Silicon Nitride | 2.00000 inch |
| 109 |
|
Ceramic Ball 2 1/8inch | 3.20-3.30 g/cm3 | 75-80 HRC | 263.46719 g | Silicon Nitride | 2.12500 inch |
| 110 |
|
Ceramic Ball 55mm G10 | 3.20-3.30 g/cm3 | 75-80 HRC | 278.76398 g | Silicon Nitride | 55.00000 mm |
| 111 |
|
Ceramic Ball 2 1/4inch | 3.20-3.30 g/cm3 | 75-80 HRC | 312.74998 g | Silicon Nitride | 2.25000 inch |
| 112 |
|
Ceramic Ball 60mm G10 | 3.20-3.30 g/cm3 | 75-80 HRC | 361.91147 g | Silicon Nitride | 60.00000 mm |
| 113 |
|
Ceramic Ball 2 3/8inch | 3.20-3.30 g/cm3 | 75-80 HRC | 367.82444 g | Silicon Nitride | 2.37500 inch |
| 114 |
|
Ceramic Ball 2 1/2inch | 3.20-3.30 g/cm3 | 75-80 HRC | 429.01232 g | Silicon Nitride | 2.50000 inch |
| 115 |
|
Ceramic Ball 65mm G10 | 3.20-3.30 g/cm3 | 75-80 HRC | 460.13860 g | Silicon Nitride | 65.00000 mm |
| 116 |
|
Ceramic Ball 2 5/8inch | 3.20-3.30 g/cm3 | 75-80 HRC | 496.63539 g | Silicon Nitride | 2.62500 inch |
| 117 |
|
Ceramic Ball 2 3/4inch | 3.20-3.30 g/cm3 | 75-80 HRC | 571.01540 g | Silicon Nitride | 2.75000 inch |
| 118 |
|
Ceramic Ball 2 7/8inch | 3.20-3.30 g/cm3 | 75-80 HRC | 652.47412 g | Silicon Nitride | 2.87500 inch |
| 119 |
|
Ceramic Ball 3inch | 3.20-3.30 g/cm3 | 75-80 HRC | 741.33330 g | Silicon Nitride | 3.00000 inch |
| 120 |
|
Ceramic Ball 3 1/4inch | 3.20-3.30 g/cm3 | 75-80 HRC | 942.54008 g | Silicon Nitride | 3.25000 inch |
| 121 |
|
Ceramic Ball 3 1/2inch | 3.20-3.30 g/cm3 | 75-80 HRC | 1177.20982 g | Silicon Nitride | 3.50000 inch |
| 122 |
|
Ceramic Ball 3 3/4inch | 3.20-3.30 g/cm3 | 75-80 HRC | 1447.91660 g | Silicon Nitride | 3.75000 inch |
| 123 |
|
Ceramic Ball 4inch | 3.20-3.30 g/cm3 | 75-80 HRC | 1757.23448 g | Silicon Nitride | 4.00000 inch |
| 124 |
|
Ceramic Ball 4 1/4inch | 3.20-3.30 g/cm3 | 75-80 HRC | 2107.73755 g | Silicon Nitride | 4.25000 inch |
| 125 |
|
Ceramic Ball 4 1/2inch | 3.20-3.30 g/cm3 | 75-80 HRC | 2501.99988 g | Silicon Nitride | 4.50000 inch |
| 126 |
|
Ceramic Ball 0.3mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00005 g | Silicon Nitride | 0.30000 mm |
| 127 |
|
Ceramic Ball 0.4mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00011 g | Silicon Nitride | 0.40000 mm |
| 128 |
|
Ceramic Ball 0.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00021 g | Silicon Nitride | 0.50000 mm |
| 129 |
|
Ceramic Ball 0.6mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00036 g | Silicon Nitride | 0.60000 mm |
| 130 |
|
Ceramic Ball 0.025inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00042 g | Silicon Nitride | 0.02500 inch |
| 131 |
|
Ceramic Ball 0.7mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00057 g | Silicon Nitride | 0.70000 mm |
| 132 |
|
Ceramic Ball 1/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00084 g | Silicon Nitride | 0.03125 inch |
| 133 |
|
Ceramic Ball 0.8mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00086 g | Silicon Nitride | 0.80000 mm |
| 134 |
|
Ceramic Ball 1mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00168 g | Silicon Nitride | 1.00000 mm |
| 135 |
|
Ceramic Ball 3/64inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00283 g | Silicon Nitride | 0.04688 inch |
| 136 |
|
Ceramic Ball 1.2mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00290 g | Silicon Nitride | 1.20000 mm |
| 137 |
|
Ceramic Ball 1.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00565 g | Silicon Nitride | 1.50000 mm |
| 138 |
|
Ceramic Ball 1/16inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.00670 g | Silicon Nitride | 0.06250 inch |
| 139 |
|
Ceramic Ball 5/64inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.01309 g | Silicon Nitride | 0.07813 inch |
| 140 |
|
Ceramic Ball 2mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.01340 g | Silicon Nitride | 2.00000 mm |
| 141 |
|
Ceramic Ball 3/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.02262 g | Silicon Nitride | 0.09375 inch |
| 142 |
|
Ceramic Ball 2.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.02618 g | Silicon Nitride | 2.50000 mm |
| 143 |
|
Ceramic Ball 7/64inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.03593 g | Silicon Nitride | 0.10938 inch |
| 144 |
|
Ceramic Ball 2.8mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.03678 g | Silicon Nitride | 2.80000 mm |
| 145 |
|
Ceramic Ball 3mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.04524 g | Silicon Nitride | 3.00000 mm |
| 146 |
|
Ceramic Ball 1/8inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.05363 g | Silicon Nitride | 0.12500 inch |
| 147 |
|
Ceramic Ball 3.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.07184 g | Silicon Nitride | 3.50000 mm |
| 148 |
|
Ceramic Ball 9/64inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.07635 g | Silicon Nitride | 0.14063 inch |
| 149 |
|
Ceramic Ball 5/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.10474 g | Silicon Nitride | 0.15625 inch |
| 150 |
|
Ceramic Ball 4mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.10723 g | Silicon Nitride | 4.00000 mm |
| 151 |
|
Ceramic Ball 4.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.15268 g | Silicon Nitride | 4.50000 mm |
| 152 |
|
Ceramic Ball 3/16inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.18099 g | Silicon Nitride | 0.18750 inch |
| 153 |
|
Ceramic Ball 5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | Silicon Nitride | 5.00000 mm | |
| 154 |
|
Ceramic Ball 5.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.27876 g | Silicon Nitride | 5.50000 mm |
| 155 |
|
Ceramic Ball 7/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.28740 g | Silicon Nitride | 0.21875 inch |
| 156 |
|
Ceramic Ball 15/64inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.35350 g | Silicon Nitride | 0.23438 inch |
| 157 |
|
Ceramic Ball 6mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.36191 g | Silicon Nitride | 6.00000 mm |
| 158 |
|
Ceramic Ball 1/4inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.42901 g | Silicon Nitride | 0.25000 inch |
| 159 |
|
Ceramic Ball 6.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.46014 g | Silicon Nitride | 6.50000 mm |
| 160 |
|
Ceramic Ball 17/64inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.51458 g | Silicon Nitride | 0.26563 inch |
| 161 |
|
Ceramic Ball 7mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.57470 g | Silicon Nitride | 7.00000 mm |
| 162 |
|
Ceramic Ball 9/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.61084 g | Silicon Nitride | 0.28125 inch |
| 163 |
|
Ceramic Ball 7.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.70686 g | Silicon Nitride | 7.50000 mm |
| 164 |
|
Ceramic Ball 5/16inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.83791 g | Silicon Nitride | 0.31250 inch |
| 165 |
|
Ceramic Ball 8mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 0.85786 g | Silicon Nitride | 8.00000 mm |
| 166 |
|
Ceramic Ball 8.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 1.02898 g | Silicon Nitride | 8.50000 mm |
| 167 |
|
Ceramic Ball 11/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 1.11526 g | Silicon Nitride | 0.34375 inch |
| 168 |
|
Ceramic Ball 9mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 1.22145 g | Silicon Nitride | 9.00000 mm |
| 169 |
|
Ceramic Ball 3/8inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 1.44792 g | Silicon Nitride | 0.37500 inch |
| 170 |
|
Ceramic Ball 10mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 1.67552 g | Silicon Nitride | 10.00000 mm |
| 171 |
|
Ceramic Ball 13/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 1.84090 g | Silicon Nitride | 0.40625 inch |
| 172 |
|
Ceramic Ball 11mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 2.23011 g | Silicon Nitride | 11.00000 mm |
| 173 |
|
Ceramic Ball 7/16inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 2.29924 g | Silicon Nitride | 0.43750 inch |
| 174 |
|
Ceramic Ball 11.5mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 2.54825 g | Silicon Nitride | 11.50000 mm |
| 175 |
|
Ceramic Ball 15/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 2.82796 g | Silicon Nitride | 0.46875 inch |
| 176 |
|
Ceramic Ball 12mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 2.89529 g | Silicon Nitride | 12.00000 mm |
| 177 |
|
Ceramic Ball 1/2inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 3.43210 g | Silicon Nitride | 0.50000 inch |
| 178 |
|
Ceramic Ball 13mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 3.68111 g | Silicon Nitride | 13.00000 mm |
| 179 |
|
Ceramic Ball 17/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 4.11667 g | Silicon Nitride | 0.53125 inch |
| 180 |
|
Ceramic Ball 14mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 4.59762 g | Silicon Nitride | 14.00000 mm |
| 181 |
|
Ceramic Ball 9/16inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 4.88672 g | Silicon Nitride | 0.56250 inch |
| 182 |
|
Ceramic Ball 15mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 5.65487 g | Silicon Nitride | 15.00000 mm |
| 183 |
|
Ceramic Ball 19/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 5.74726 g | Silicon Nitride | 0.59375 inch |
| 184 |
|
Ceramic Ball 5/8inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 6.70332 g | Silicon Nitride | 0.62500 inch |
| 185 |
|
Ceramic Ball 16mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 6.86291 g | Silicon Nitride | 16.00000 mm |
| 186 |
|
Ceramic Ball 21/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 7.75993 g | Silicon Nitride | 0.65625 inch |
| 187 |
|
Ceramic Ball 17mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 8.23181 g | Silicon Nitride | 17.00000 mm |
| 188 |
|
Ceramic Ball 11/16inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 8.92212 g | Silicon Nitride | 0.68750 inch |
| 189 |
|
Ceramic Ball 18mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 9.77161 g | Silicon Nitride | 18.00000 mm |
| 190 |
|
Ceramic Ball 23/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 10.19491 g | Silicon Nitride | 0.71875 inch |
| 191 |
|
Ceramic Ball 19mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 11.49236 g | Silicon Nitride | 19.00000 mm |
| 192 |
|
Ceramic Ball 3/4inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 11.58333 g | Silicon Nitride | 0.75000 inch |
| 193 |
|
Ceramic Ball25/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 13.09242 g | Silicon Nitride | 0.78125 inch |
| 194 |
|
Ceramic Ball 20mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 13.40413 g | Silicon Nitride | 20.00000 mm |
| 195 |
|
Ceramic Ball 13/16inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 14.72719 g | Silicon Nitride | 0.81250 inch |
| 196 |
|
Ceramic Ball 21mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 15.51695 g | Silicon Nitride | 21.00000 mm |
| 197 |
|
Ceramic Ball 27/32inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 16.49267 g16.49267 g | Silicon Nitride | 0.84375 inch |
| 198 |
|
Ceramic Ball 22mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 17.84089 g | Silicon Nitride | 22.00000 mm |
| 199 |
|
Ceramic Ball 7/8inch G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 18.39390 g | Silicon Nitride | 0.87500 inch |
| 200 |
|
Ceramic Ball 23mm G5 | 3.20-3.30 g/cm3 | 75-80 HRC | 20.38600 g | Silicon Nitride | 23.00000 mm |
1. Применение керамических шаров
Керамические шарики имеют широкий спектр применения в промышленности и повседневной жизни, в основном включая:
Подшипники: Керамические шарики часто используются для производства различных прецизионных подшипников, особенно высокоскоростных и высоконагруженных. Керамические подшипники имеют более низкий коэффициент трения, более высокую коррозионную стойкость и устойчивость к высоким температурам, чем стальные шарикоподшипники.
Мелющие среды: Керамические шарики могут использоваться в качестве мелющих сред при дроблении и измельчении. Они широко используются в таких отраслях, как химия, фармацевтика и горнодобывающая промышленность, особенно когда требуется высокая твердость и износостойкость.
Уплотнения: Керамические шарики также широко используются в области уплотнения жидкостей и газов, особенно когда требуется устойчивость к высокой температуре или коррозии.
Фильтрация: Некоторые керамические шарики используются в системах фильтрации, особенно в процессах водоподготовки и очистки отходящих газов, где они могут эффективно удалять примеси и частицы.
Электронные компоненты: В некоторых высокотехнологичных областях керамические шарики используются в производстве высокоточных электронных компонентов, таких как датчики и конденсаторы.
2. Характеристики керамических шаров
Сильная износостойкость: Керамические шарики обладают очень высокой твердостью, что позволяет эффективно снизить износ и увеличить срок службы оборудования.
Хорошая коррозионная стойкость: Керамические шарики обладают сильной коррозионной стойкостью к химическим веществам, таким как кислоты, щелочи и соли, и подходят для работы в экстремальных условиях.
Хорошая устойчивость к высоким температурам: Керамические материалы выдерживают более высокие температуры, чем металлы, и подходят для высокотемпературных рабочих сред.
Легкий вес: Керамические шарики обычно легче металлических и иногда могут эффективно снижать вес всей конструкции, что делает их подходящими для некоторых применений, требующих малого веса.
Снижение трения: Керамические шарики обычно имеют более низкий коэффициент трения, чем металлические, что особенно важно для некоторых высокоскоростных устройств.